Graphene features high thermal conductivity

Posted: 17 Nov 2011  Print Version  Bookmark and Share

Keywords:UV LED  few-layer graphene  thermal conductivity 

Researchers from South Korea and U.S. reveal high electrical and thermal conductivities of graphene, in addition to the transparency it offers for UV LEDs.

Researchers have looked at the capabilities of few-layer graphene (FLG) as a transparent conducting layer for ultraviolet (UV) nitride semiconductor LEDs. In an article written by Mike Cooke, the study that included Korea University, Korea Electronics Technology Institute and the U.S. Naval Research Laboratory has shown promising results.

The FLG material used for nitride LED contacts was first grown on copper (Cu) foil using chemical vapour deposition (CVD) and coated with Polymethyl methacrylate (PMMA) thermoplastic. The FLG film was then separated with the PMMA layer from the copper using a six-hour wet etch in 1%-by-weight ammonium persulfate ((NH4)2S2O8) solution. The FLG/PMMA was finally floated onto the top p-contact of UV nitride semiconductor LED structures that had been grown with metal-organic chemical vapour deposition. The single-quantum-well active light-emitting region consisted of 5nm GaN sandwiched between 8nm AlGaN barriers. The p-GaN consisted of 200nm magnesium-doped material.

few-layer graphene

Schematic of the processes used to fabricate UV LED with a graphene-based transparent conductive electrode. FLG on the Cu foil was grown by CVD. (a) PMMA was coated on the graphene layer. (b) Cu foil on the graphene layer was removed by wet etching in ammonium persulfate. (c) Graphene with PMMA was deposited on p-GaN layer and PMMA was removed. (d) LED chips were fabricated by standard photolithographic processes.

The mesa structure of the LED was created after FLG transfer using plasma etch of boron trichloride and chlorine gas. The ohmic n-electrode consisted of 750°C annealed titanium-aluminium-nickel gold. Contact pads consisted of titanium-gold for both n- and p-type connections.

One advantage of using graphene over indium tin oxide (ITO) as transparent conductive oxide is its improved transmission in UV. At 372nm, the transmittances of bi- (2L) and tetra-layer (4L) graphene were found to be 95 per cent and 89 per cent, respectively. By contrast, the value for 150nm ITO was 68 per cent. This advantage for graphene lessens for longer wavelengths and disappears around 600nm.

The survival of the graphene layer from the LED process was confirmed by Raman spectroscopy that also determined the number of layers by comparing the intensity of the peaks from the G and 2D bands arising from vibration/phonon modes.

The effect of using a 4L-graphene transparent contact was to double the injection current in LEDs. At 10V bias, an LED without graphene p-contact carried 2.3mA, and with the 4L-graphene, it carried 5mA. The main UV emission at 20mA occurs at 372nm. The broad green-yellow (500-600nm) emission is attributed to 'nitrogen vacancy and other growth related defects in the GaN.' Increased light output was also seen for 20mW input power. Without graphene, light is only emitted from the edges of the structure. The 4L-graphene acts to spread the injection current and cause the whole device to emit.

spectra of UV LEDs

(a) The I–V characteristics of the UV LED with and without FLG-based transparent conductive electrode. (b)The EL spectra of UV LEDs. Optical images of light emission of UV LEDs (c) without and (d) with FLG-based transparent conductive electrode.

There is a trade-off between the conductivity of graphene and transparency. Thicker layers are more conductive, but transmit less UV.

The FLG contact LED could sustain 10mW input power for an 'extended period of time.' However, increasing to 20mW reduced light output. The emission pattern that resulted was similar to that of the LED without FLG transparent conductive layer, suggesting that high-power operation removed the graphene layer. Raman spectroscopy investigation suggested that after a minute, the 4L layer had been reduced to 2L, which is less effective at spreading the injection current due to its lower conductivity.

"This study confirms that graphene-based transparent contact to a GaN-based UV LED is superior to an ITO contact based on cost, transparency, and heat and current spreading. However, critical issues such as reliability and degradation of graphene films require and are the subject of further investigation," the researchers concluded.





Comment on "Graphene features high thermal condu..."
Comments:  
*  You can enter [0] more charecters.
*Verify code:
 
 
 
Webinars

Seminars

Visit Asia Webinars to learn about the latest in technology and get practical design tips.

 

Go to top             Connect on Facebook      Follow us on Twitter      Follow us on Orkut

 
Back to Top